Compressive Strength and Thermal Conductivity of Porous Mullite Ceramics

https://doi.org/10.22146/jmpc.51410

Muhammad Waziz Wildan(1*), F Marpaung(2)

(1) Department of Mechanical and Industrial Engineering, Faculty of Engineering, Universitas Gadjah Mada. Jl. Grafika 2, Yogyakarta 55281, Indonesia
(2) Department of Mechanical and Industrial Engineering, Faculty of Engineering, Universitas Gadjah Mada. Jl. Grafika 2, Yogyakarta 55281, Indonesia
(*) Corresponding Author

Abstract


Porous ceramics are a form of ceramic material with widespread applications, such as filters, isolators, and acoustics. This research aimed to investigate the compressive strength and thermal conductivity of porous mullite ceramics (3Al2O3.2SiO2 or Si2Al6O13) produced using dry yeast powder as a PFA (pore-forming agent). Kaolin powder (Al2O3.2SiO4.2H2O or Al2Si2O5(OH)4) was used as a raw material for producing mullite ceramics. Kaolin powder and dry yeast powder were mixed at a variety of dry yeast powder weight fractions: 0%, 5%, 10%, 15%, 20%, and 25%. The composition was mixed using Turbula Mixer for 1 hour. The cylindrical green body (diameters of 12 mm, 15 mm, and 30 mm) of every constituent was formed by the uniaxial pressing method at 10 MPa. Monolithic kaolin was sintered at variable temperatures (1,100 oC, 1,200 oC, 1,300 oC, 1,400 oC, 1,450 oC) for 2 hours then subjected to several tests for its density. From the bulk density tests, it was found that the optimum temperature for 2-hour sintering was 1,450 oC. This temperature was then used for the sintering process of the kaolin specimens which contained dry yeast powder. Testing was performed on the microstructure, bulk density, burning waste in mass and volume, compressive strength, and thermal conductivity. According to the literature, kaolin will transform into mullite (3Al2O3.2SiO2 or Si2Al6O13) and cristobalite (SiO2) at 1,450 oC. It was found that with the increase in the content of dry yeast powder as PFA in the mixture with kaolin, the bulk density decreased (from 2.44 gr/cm3 to 1.521 gr/cm3), the porosity increased (from 23.77% to 52.48%), the compressive strength decreased (from 38.04 MPa to 4.51 MPa), and the thermal conductivity decreased (from 3.76 W/moC to1.34 W/moC), each from yeast powder content 0% to 25%.


Keywords


kaolin, mullite, dry yeast powder, porosity, compressive strength, thermal conductivity, PFA (pore-forming agent).

Full Text:

PDF


References

Barsoum, M, 2003, Fundamentals of Ceramics, McGraw Hill, Singapore

Chen, C.Y. & Tuan, W.H., 2001, “The Processing of Kaolin Powder Compact”, Ceramics Internationals (27), 795-800.

Chen, C.H., Takita, K., Ishiguro, S., Honda, S., Awaji, H., 2005, Fabrication of porous alumina tube by centrifugal molding, J. Eur. Ceram. Soc., 25(4), pp. 3257-3264.

Cristobalite data, http://webmineral.com/data/Cristobalite.shtml#.W9Ot1pMzY2w

Gregorova, E., Pabst, W, 2006, Porous ceramics prepared using poppy seed as pore-forming agent, Ceramics International.

Gregorova, E., Pabst, and Bohacenko, I, 2006, Characterization of different starch types for their application in ceramic processing, J. Eur. Ceram. Soc., 26 (8), pp.1301-1309.

Hammel E.C, Ighodaro, O.L.R, dan Okoli, O,I, 2014, Processing and properties of advanced porous ceramic: an application based review, Ceramics International, Vol 40(10), pp. 15351-15370

Kingon, A. I., & Davis, R.F., 2000, Engineering Properties of Multi-Component and Multiphase Oxides, in Ceramics and Glasses, Engineered Materials Handbook, Vol.4., ASM Inter-national, 758-774.

Lee, W.E. & Rainforth, W.M., 1994, Ceramic Microstructures Property Control by Prosessing, Chapman & Hall, Sheffield University.

Liu, P.S., dan Chen, G.F., Porous Materials, Processing and Applications, Tsinghwa University Press. 2014.

Manap, N.R.A, dan Jais, U.S., 2009, Influence of concentration of pore forming agent on porosity of SiO2 ceramic from rice husk, Material Research Innovations, Vol 13(3), pp.382-385.

Mullite data, http://webmineral.com/data/ mullite.shtml#.W9Otc5MzY2w

Sandra, K., Budi, A., dan Susilo, A. (2014). Pengaruh Suhu Sintering Terhadap Densitas dan Porositas pada Membran Keramik Berpori Berbasis Zeolit, Tanah Lempung, Arang Batok Kelapa dan PVA. Jurnal Fisika, Fakultas Matematika dan Ilmu Pengetahuan Alam, Universitas Negeri Jakarta.

Wildan, MW, Suhanan dan Darwanto, 2009, Thermal conductivity and bending strength of porous mullite ceramics made by PFA method using corn starch, Jurnal Teknik Mesin ITS, Vol 9(3), hal. 149-155.



DOI: https://doi.org/10.22146/jmpc.51410

Article Metrics

Abstract views : 2446 | views : 2002

Refbacks

  • There are currently no refbacks.