Hydrochloric Acid and/or Sodium Hydroxide-modified Zeolite Y for Catalytic Hydrotreating of α-Cellulose Bio-Oil


Jason Mandela(1), Wega Trisunaryanti(2*), Triyono Triyono(3), Mamoru Koketsu(4), Dyah Ayu Fatmawati(5)

(1) Department of Chemistry, Faculty of Mathematics and Natural Sciences, Universitas Gadjah Mada, Sekip Utara, Yogyakarta 55281, Indonesia
(2) Department of Chemistry, Faculty of Mathematics and Natural Sciences, Universitas Gadjah Mada, Sekip Utara, Yogyakarta 55281, Indonesia
(3) Department of Chemistry, Faculty of Mathematics and Natural Sciences, Universitas Gadjah Mada, Sekip Utara, Yogyakarta 55281, Indonesia
(4) Department of Chemistry and Biomolecular Science, Faculty of Engineering, Gifu University, 1-1 Yanagido, Gifu 501-1193 Japan
(5) Department of Chemistry, Faculty of Mathematics and Natural Sciences, Universitas Gadjah Mada, Sekip Utara, Yogyakarta 55281, Indonesia
(*) Corresponding Author


The zeolite Y had been successfully modified by HCl and/or NaOH treatment. The modification of zeolite Y was performed by leaching the protonated zeolite Y (HY) in HCl solution (0.1 and 0.5 M) at 70 °C for 3 h resulting in DY0.1 and DY0.5. Subsequently, HY, DY0.1, and DY0.5 zeolites were immersed in 0.1 M NaOH for 15 min at room temperature resulting in AHY, ADY0.1, and ADY0.5. All samples were analyzed for acidity, crystallinity, Si/Al ratio, morphology, and textural properties. The catalytic performance of all samples was investigated in hydrotreating of α-cellulose bio-oil with a catalyst/feed weight ratio of 1/30. The HCl and NaOH treatment led to the decrease of the zeolite Y crystallinity and the increase of the zeolite Y average pore diameter (i.e., the mesopore distribution). The ADY0.5 gave the highest mesopore distribution, which was 43.7%, with an average pore diameter of 4.59 nm. Moreover, both of the treatments were found to increase the Si/Al ratio that caused the decrease of zeolites Y acidity. All the zeolite Y samples gave better catalytic activity to produce liquid products after being treated by NaOH. The sample ADY0.5 managed to produce 6.12% of 1-isopropyl-2,4-dimethylbenzene that has good potential to be processed into fuel.


HCl treatment; mesoporous structure; NaOH treatment; pyrolyzed α-cellulose hydrotreatment

Full Text:

Full Text PDF


[1] Khowatimy, F.A., Priastomo, Y., Febriyanti, E., Riyantoko, H., and Trisunaryanti, W., 2014, Study of waste lubricant hydrocracking into fuel fraction over the combination of Y-zeolite and ZnO catalyst, Procedia Environ. Sci., 20, 225–234.

[2] Zhao, J., Wang, G., Qin, L., Li, H., Chen, Y., and Liu, B., 2016, Synthesis and catalytic cracking performance of mesoporous zeolite Y, Catal. Commun., 73, 98–102.

[3] Verboekend, D., Nuttens, N., Locus, R., Van Aelst, J., Verolme, P., Groen, J.C., Pérez-Ramírez, J., and Sels, B.F., 2016, Synthesis, characterisation, and catalytic evaluation of hierarchical faujasite zeolites: Milestones, challenges, and future directions, Chem. Soc. Rev., 45 (12), 3331–3352.

[4] Lutz, W., 2014, Zeolite Y: Synthesis, modification, and properties–A case revisited, Adv. Mater. Sci. Eng., 2014, 724248.

[5] Tian, F., Wu, Y., Shen, Q., Li, X., Chen, Y., and Meng, C., 2013, Effect of Si/Al ratio on mesopore formation for zeolite beta via NaOH treatment and the catalytic performance in α-pinene isomerization and benzoylation of naphthalene, Microporous Mesoporous Mater., 173, 129–138.

[6] Wu, Y., Tian, F., Liu, J., Song, D., Jia, C., and Chen, Y., 2012, Enhanced catalytic isomerization of α-pinene over mesoporous zeolite beta of low Si/Al ratio by NaOH treatment, Microporous Mesoporous Mater., 162, 168–174.

[7] Hernawan, Wahono, S.K., Maryana, R., and Pratiwi, D., 2015, Modification of Gunungkidul natural zeolite as bioethanol dehydrating agents, Energy Procedia, 65, 116–120.

[8] Mara, A., Wijaya, K., Trisunaryanti, W., and Mudasir, 2016, Effect of sulfuric acid treatment and calcination on natural zeolites of Indonesia, Asian J. Chem., 28, 11–14.

[9] Pongsendana, M., Trisunaryanti, W., Artanti, F.W., Falah, I.I., and Sutarno, 2017, Hydrocracking of waste lubricant into gasoline fraction over CoMo catalyst supported on mesoporous carbon from bovine bone gelatin, Korean J. Chem. Eng., 34 (10), 2591–2596.

[10] Silaghi, M.C., Chizallet, C., and Raybaud, P., 2014, Challenges on molecular aspects of dealumination and desilication of zeolites, Microporous Mesoporous Mater., 191, 82–96.

[11] García, J.R., Falco, M., and Sedran, U., 2016, Impact of the desilication treatment of Y zeolite on the catalytic cracking of bulky hydrocarbon molecules, Top. Catal., 59 (2), 268–277.

[12] Groen, J.C., Sano, T., Moulijn, J.A., and Pérez-Ramírez, J., 2007, Alkaline-mediated mesoporous mordenite zeolites for acid-catalyzed conversions, J. Catal., 251 (1), 21–27.

[13] Chu, S., Yang, L., Guo, X., Dong, L., Chen, X., Li, L., and Mu, X., 2018, The influence of pore structure and Si/Al ratio of HZSM-5 zeolites on the product distributions of α-cellulose hydrolysis, Mol. Catal., 445, 240–247.

[14] Bartoli, M., Rosi, L., Giovannelli, A., Frediani, P., and Frediani, M., 2016, Pyrolysis of α-cellulose using a multimode microwave oven, J. Anal. Appl. Pyrolysis., 120, 284–296.

[15] Lin, Y.C., Cho, J., Tompsett, G.A., Westmoreland, P.R., and Huber, G.W., 2009, Kinetics and mechanism of cellulose pyrolysis, J. Phys. Chem. C, 113 (46), 20097–20107.

[16] Zhao, C., Jiang, E., and Chen, A., 2017, Volatile production from pyrolysis of cellulose, hemicellulose, and lignin, J. Energy Inst., 90 (6), 902–913.

[17] Marsuki, M.F., Trisunaryanti, W., Falah, I.I., and Wijaya, K., 2018, Synthesis of Co, Mo, Co-Mo, and Mo-Co catalysts, supported on mesoporous silica-alumina for hydrocracking of a-cellulose pyrolysis oil, Orient. J. Chem., 34 (2), 955–962.

[18] Groen, J.C., Peffer, L.A.A., Moulijn, J.A., and Pérez-Ramírez, J., 2005, Mechanism of hierarchical porosity development in MFI zeolites by desilication: The role of aluminium as a pore-directing agent, Chemistry, 11 (17), 4983–4994.

[19] Si, Z., Zhang, X., Wang, C., Ma, L., and Dong, R., 2017, An overview on catalytic hydrodeoxygenation of pyrolysis oil and its model compounds, Catalysts, 7 (6), 169.

[20] Vogt, E.T.C., and Weckhuysen, B.M., 2015, Fluid catalytic cracking: Recent developments on the grand old lady of zeolite catalysis, Chem. Soc. Rev., 44 (20), 7342–7370.

DOI: https://doi.org/10.22146/ijc.55645

Article Metrics

Abstract views : 6918 | views : 4139

Copyright (c) 2020 Indonesian Journal of Chemistry

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.


Indonesian Journal of Chemistry (ISSN 1411-9420 /e-ISSN 2460-1578) - Chemistry Department, Universitas Gadjah Mada, Indonesia.

Analytics View The Statistics of Indones. J. Chem.